Families>
Alloyed and Refractory Steels > Electrodes
|
Soder 86
- Alloyed steels
|
|
Special rutile covered electrode for junction and recharge on alloyed steels and cast iron against soft iron. Suitable for first passes under hard electrodes recharges.
|
| Elongation |
26%
|
| Resiliency |
80
|
| Current |
DC (+) or AC
|
| Hardness |
240 Hb workable
|
|
Request more information
|
|
Soder 174
- Against corrosion
|
|
Special electrode for "hastelloy c" or AISI 316 - 309 mo when high temperature and corrosion endurance is needed. Very good weldabilty and beautiful shape of passes, austenitic
|
| Elongation |
14%
|
| Resiliency |
75
|
| Current |
DC (+) or AC
|
| Hardness |
200 Hb
|
|
Request more information
|
|
Soder 30
- Cracks
|
|
Synthetic basic coated electrode for junctions between refractory steels "Inconel 82" with exercise temperatures from -196C to +1400C. Well suited also for vertical or square welding of forged - iron or steel with cracks to repair. Suitable for cracks in forging moulds and tools, creusabro weld, ovens maintenance and for hydraulic press repair.
|
| Strength |
-196 C: 55Jkg/mm2
|
| Elongation |
35%
|
| Resiliency |
68
|
| Current |
DC (+)
|
|
Request more information
|
|
Soder 174HL
- Elasticity
|
|
High recovery (160%) electrode for recharges and unions on manganese steels and hard steels castings. It gets harder under shocks but at first, as welded, it`s soft for filing. Suitable also for strong solicitations thanks to the great elasticity.
|
| Elongation |
40%
|
| Resiliency |
70
|
| Current |
DC (+) or AC
|
| Hardness |
230 Hb workable / 500 after shocks
|
|
Request more information
|
|
Soder 85
- Versatility
|
|
Easy - weld electrode and low amperage suitable for hard steel machinable and soft for file recharge, good also for dissimilar joints or unknowing steels, vertical and pipes welding for high pressure, passes without porosity or cracks.
|
| Elongation |
29%
|
| Resiliency |
82
|
| Current |
DC (+) or AC
|
| Hardness |
240 Hb workable / 400 after shocks
|
|
Request more information
|
|